KASHIN KIMIYYA:
ALOY(wt%) | C | Mn | Si | Ni | Fe | Ti | Cu | P | S |
GB/T dokokin | 0.10 | 0.75 | 1.20 | ≥92 | 0.70 | 1.0-4.0 | 0.20 | 0.02 | 0.015 |
Dokokin AWS | 0.10 | 0.75 | 1.25 | ≥92 | 0.75 | 1.0-4.0 | 0.25 | 0.03 | 0.02 |
MISALI DARAJAR | 0.046 | 0.06 | 0.82 | 95.5 | 0.12 | 2.7 | 0.01 | 0.007 | 0.001 |
DUKIYAR INJI:
DUKIYA | KARFIN KYAUTA (MPa) | KARFIN ARZIKI(MPa) | IMAPACT DARAJAR J/℃ | LONGATION(%) | ||||
GB/T dokokin | 200 | 410 | - | 18 | ||||
Dokokin AWS | - | 410 | - | 20 | ||||
MISALI DARAJAR | 310 | 435 | - | 29 |
SHAWARAR ALAMOMIN welding:
BAYANIN DIAMETERS(mm) | 2.6*300 | 3.2*350 | 4.0*350 | |||||||
WUTAR LANTARKI (Amp) | H/W | 65-95 | 70-115 | 95-145 |
Titanium-calcium electrode hand electrode, nominal abun da ke ciki (kashi bisa nauyi) shine 95Ni-2.5Ti.
Tsayayyen baka, kyakkyawan tsari, ɗan fantsama, sauƙin cire slag, juriya mai kyau.
Ƙarfe mai haɗaka yana da kyawawan kaddarorin inji, juriya na zafi, juriya na lalata, haɗuwa da juriya.
Cr-Mo karfe jerin kayan waldawa da kayan waldawa na lantarki ana amfani da su sosai a cikin kayan aikin tace mai.
-
Tankar Suez tan 158,000
Supercore SG
KASHIN KIMIYYA:
ALOY(wt%) | C | Mn | Si | Ni | Fe | Ti | Cu | P | S |
GB/T dokokin | 0.10 | 0.75 | 1.20 | ≥92 | 0.70 | 1.0-4.0 | 0.20 | 0.02 | 0.015 |
Dokokin AWS | 0.10 | 0.75 | 1.25 | ≥92 | 0.75 | 1.0-4.0 | 0.25 | 0.03 | 0.02 |
MISALI DARAJAR | 0.046 | 0.06 | 0.82 | 95.5 | 0.12 | 2.7 | 0.01 | 0.007 | 0.001 |
DUKIYAR INJI:
DUKIYA | KARFIN KYAUTA (MPa) | KARFIN ARZIKI(MPa) | IMAPACT DARAJAR J/℃ | LONGATION(%) | ||||
GB/T dokokin | 200 | 410 | - | 18 | ||||
Dokokin AWS | - | 410 | - | 20 | ||||
MISALI DARAJAR | 310 | 435 | - | 29 |
SHAWARAR ALAMOMIN welding:
BAYANIN DIAMETERS(mm) | 2.6*300 | 3.2*350 | 4.0*350 | |||||||
WUTAR LANTARKI (Amp) | H/W | 65-95 | 70-115 | 95-145 |