AWS E7018-A1 Low-alloy steels Karfe foda waldi waya na'urorin haɗi
Aikace-aikace & Standard&Lura:
AWS E7018-A1 (R106Fe) zafi-resistant karfe hannun electrode dace waldi tukunyar jirgi bututu, zafi Exchanger dumama surface bututu da tururi bututu kasa 450 ℃ (kamar 15MoG, T1, P1 karfe) da sauran lokatai.Irin su ASTM A204 da A335-P1 bututu;A weldment ya kamata a preheated zuwa 90-110 ℃ kafin waldi, da kuma kula da interlayer zafin jiki.Haka kuma za a iya amfani da waldi janar low gami karfe high ƙarfi karfe tsarin.Kuma ana iya amfani da wannan na'urar lantarki ta hannu don cikakken walƙiya.Bisa ga halaye na samar da tsari na low-zazzabi liquefied gas, da low-zazzabi karfe da ake amfani da daban-daban maki bisa ga daban-daban sabis yanayin zafi (-40 ℃, -70 ℃, -100 ℃, -194 ℃, -253 ℃). ), kuma an zaɓi kayan walda masu dacewa.
Siffofin
Irin wannan na'urar lantarki ta hannu ita ce foda baƙin ƙarfe low nau'in lantarki na hannu, yana ƙara foda na ƙarfe, ingantaccen narkewa;0.5% Mo an ƙara don inganta ƙarfin weld da juriya na lalata;Kuma baka ya tsaya tsayin daka, kasa fantsama, kafawa, desagging abu ne mai sauki, aikin X-Ray yana da kyau.
Abubuwan da aka haɗa na yau da kullun na pearlitic zafi resistant karfe sune chromium, molybdenum, vanadium, niobium da sauransu don saduwa da buƙatun aiki daban-daban.Saboda aikin haɗin gwiwa na abubuwan haɗin gwiwar carbon a cikin ƙarfe, yana da sauƙi don samar da tsari mai tauri a lokacin waldi, kuma aikin walda ba shi da kyau.Don haka, karfe mai jure zafi na pearlitic gabaɗaya ana preheated kafin waldawa da zafin rai bayan walda.
Kamfanin & Factory
Gabatarwar abun da ke ciki da kayan aikin injiniya
Gabatarwar abun da ke ciki da kayan aikin injiniya
KASHIN KIMIYYA:
ALOY(wt%) | C | Mn | Si | Cr | Mo | P | S |
GB/T dokokin | 0.12 | 1.00 | 0.80 | - | 0.40-0.65 | 0.03 | 0.030 |
Dokokin AWS | 0.12 | 0.90 | 0.80 | - | 0.40-0.65 | 0.03 | 0.030 |
MISALI DARAJAR | 0.6 | 0.7 | 0.31 | 0.035 | 0.5 | 0.012 | 0.01 |
DUKIYAR INJI:
DUKIYA | KARFIN KYAUTA (MPa) | KARFIN ARZIKI(MPa) | MAGANIN ZAFIN ℃xh | IMAPACT DARAJAR J/℃ | LONGATION(%) | |||||||||
GB/T dokokin | 390 | 490 | 620*1 | - | 22 | |||||||||
Dokokin AWS | 390 | 490 | 620*1 | - | 22 | |||||||||
MISALI DARAJAR | 480 | 570 | 620*1 | 170/Yawan zafin jiki | 26 |
SHAWARAR ALAMOMIN welding:
BAYANIN DIAMETERS(mm) | 2.6*350 | 3.2*350 | 4.0*400 | 5.0*400 | ||||||
WUTAR LANTARKI (Amp) | H/W | 80-110 | 100-130 | 130-180 | 170-210 | |||||
O/W | 60-100 | 80-120 | 120-160 | - |
BAYANIN CIKI:
SANARWA | TSORO | PCS/1KG | NUNA/1KG | |||
2.6mm | 300mm | 48 PCS | 2KG | |||
3.2mm | mm 350 | 27 PCS | 5KG | |||
4.0mm | mm 350 | 16 PCS | 5KG | |||
5.0mm ku | mm 350 | 12 PCS | 5KG |
Al'amuran Al'ada
Takaddun shaida
Gabatarwar abun da ke ciki da kayan aikin injiniya
KASHIN KIMIYYA:
ALOY(wt%) | C | Mn | Si | Cr | Mo | P | S |
GB/T dokokin | 0.12 | 1.00 | 0.80 | - | 0.40-0.65 | 0.03 | 0.030 |
Dokokin AWS | 0.12 | 0.90 | 0.80 | - | 0.40-0.65 | 0.03 | 0.030 |
MISALI DARAJAR | 0.6 | 0.7 | 0.31 | 0.035 | 0.5 | 0.012 | 0.01 |
DUKIYAR INJI:
DUKIYA | KARFIN KYAUTA (MPa) | KARFIN ARZIKI(MPa) | MAGANIN ZAFIN ℃xh | IMAPACT DARAJAR J/℃ | LONGATION(%) | |||||||||
GB/T dokokin | 390 | 490 | 620*1 | - | 22 | |||||||||
Dokokin AWS | 390 | 490 | 620*1 | - | 22 | |||||||||
MISALI DARAJAR | 480 | 570 | 620*1 | 170/Yawan zafin jiki | 26 |
SHAWARAR ALAMOMIN welding:
BAYANIN DIAMETERS(mm) | 2.6*350 | 3.2*350 | 4.0*400 | 5.0*400 | ||||||
WUTAR LANTARKI (Amp) | H/W | 80-110 | 100-130 | 130-180 | 170-210 | |||||
O/W | 60-100 | 80-120 | 120-160 | - |
BAYANIN CIKI:
SANARWA | TSORO | PCS/1KG | NUNA/1KG | |||
2.6mm | 300mm | 48 PCS | 2KG | |||
3.2mm | mm 350 | 27 PCS | 5KG | |||
4.0mm | mm 350 | 16 PCS | 5KG | |||
5.0mm ku | mm 350 | 12 PCS | 5KG |