430Mpa Hannun Electrode Don Ƙananan Karfe Carbon
Aikace-aikace & Standard&Lura:
1. Welding talakawa ƙarfi na low carbon karfe tsarin da low ƙarfi sa na low gami karfe.
2. Matsayin da muka hadu: GB/T5117 E4303, AWS, ISO2560-A: E 35 0 R 1 2, ISO 2560-B: E4303A, JIS Z3211 E4303
1. Dole ne a dafa insulator, kuma dole ne a gasa wutar lantarki a 180 ° C. Lokacin da ake walda shi a cikin bitar, yana buƙatar sanya shi a cikin silinda mai rufewa.
2. Kulawa lokacin walda: Don tabbatar da cewa yankin walda yana da tsabta, yana da mahimmanci a cire duk wani mai ko wasu gurɓata daga radius 20mm a kusa da walda kafin walda. Welds dole ne su kasance masu tsabta, masu haske, kuma marasa lalacewa. Ana buƙatar nau'in walda mai kyau (bisa ga aikin waldawa da hannu) 3. Yanayin walda, gami da iska da ƙura. Kula da hankali sosai, 4, ƙimar walda: tsayin sandar walda na yau da kullun shine 40CM."
Siffofin
1. Titanium calcium type c hemical fata carbon karfe electrode.
2. Stable arc, mai kyau slag fluidity, sauki slag cire, kananan fantsama, kyakkyawan siffar.
Sunan Sinanci na GEM-F03 low carbon hand electrode shine J422, yayin da alamar ƙasa da ƙasa ita ce E4303. J yana nufin tsarin lantarki na ƙarfe, 42 yayi daidai da 420 kg/mm2, kuma yana nuna ƙarfin jujjuyawar ƙarfen weld. Ita ce electrode acid na nau'in calcium mai rufi na titanium. Amfani da waldi LOW carbon karfe Tsarin da low ƙarfi maki na low gami karfe, fiye amfani da waldi karfe Tsarin da misali carbon karfe bututu."
Kamfanin & Factory
Gabatarwar abun da ke ciki da kayan aikin injiniya
KASHIN KIMIYYA:
| ALOY(wt%) | C | Mn | Si | Cr | Ni | Mo | P | S | V |
| GB/T dokokin | 0.2 | 1.2 | 1 | 0.2 | 0.3 | 0.3 | 0.04 | 0.035 | 0.08 |
| Dokokin AWS | - | - | - | - | - | - | - | - | - |
| MISALI DARAJAR | 0.076 | 0.5 | 0.38 | 0.025 | 0.01 | 0.028 | 0.016 | 0.01 | 0.008 |
DUKIYAR INJI:
| DUKIYA | KARFIN KYAUTA (MPa) | KARFIN ARZIKI(MPa) | MAGANIN ZAFIN ℃xh | ||||||
| GB/T dokokin | 330 | 430 | AW | ||||||
| Dokokin AWS | - | - | AW | ||||||
| MISALI DARAJAR | 468 | 538 | AW | ||||||
SHAWARAR ALAMOMIN welding:
| BAYANIN DIAMETERS(mm) | 2.6*350 | 3.2*350 | 4.0*400 | 5.0*400 | |||||
| WUTAR LANTARKI | H/W | 80-120 | 90-140 | 150-190 | 180-240 | ||||
| (Amp) | O/W | 50-80 | 90-120 | 130-160 | - | ||||
NOTE:
H/W: a kwance matsayi waldi
O/W: walƙiya matsayi sama da kai
Al'amuran Al'ada
Takaddun shaida
Gabatarwar abun da ke ciki da kayan aikin injiniya
KASHIN KIMIYYA:
| ALOY(wt%) | C | Mn | Si | Cr | Ni | Mo | P | S | V |
| GB/T dokokin | 0.2 | 1.2 | 1 | 0.2 | 0.3 | 0.3 | 0.04 | 0.035 | 0.08 |
| Dokokin AWS | - | - | - | - | - | - | - | - | - |
| MISALI DARAJAR | 0.076 | 0.5 | 0.38 | 0.025 | 0.01 | 0.028 | 0.016 | 0.01 | 0.008 |
DUKIYAR INJI:
| DUKIYA | KARFIN KYAUTA (MPa) | KARFIN ARZIKI(MPa) | MAGANIN ZAFIN ℃xh | ||||||
| GB/T dokokin | 330 | 430 | AW | ||||||
| Dokokin AWS | - | - | AW | ||||||
| MISALI DARAJAR | 468 | 538 | AW | ||||||
SHAWARAR ALAMOMIN welding:
| BAYANIN DIAMETERS(mm) | 2.6*350 | 3.2*350 | 4.0*400 | 5.0*400 | |||||
| WUTAR LANTARKI | H/W | 80-120 | 90-140 | 150-190 | 180-240 | ||||
| (Amp) | O/W | 50-80 | 90-120 | 130-160 | - | ||||
NOTE:
H/W: a kwance matsayi waldi
O/W: walƙiya matsayi sama da kai